▪ Technical
MULTIS 400+ Specs.
Three layers.
Two working faces.
Face. PVC composite surface that meets the concrete.
Core. Reinforced solid PVC composite.
Second face. So the board can be turned over.
Made to order for your panel system, 10–23 mm thick and up to 6,000 × 2,050 mm.
For technical queries please email
▪ technical@multiseu.com
| Technical properties | Test method | Specifications | |||
|---|---|---|---|---|---|
| Dimensions (mm) | N/A | Variable as per request Length: up to 6,000 mm, Width: up to 2,050 mm Thickness: 10 mm up to 23 mm in 0.5 mm increments | |||
| Tolerance | N/A | Length: ±0.5 mm/m, Width: ±0.5 mm/m, Thickness: ±0.3 mm | |||
| Board thickness | 10 mm | 11 mm | 15.5 mm | 19 mm | |
| Flexural strength (MPa) | ISO 178:2019 Method A | 30.8 | 33.1 | 33.7 | 40.0 |
| Flexural modulus (MPa) | ISO 178:2019 Method A | 3,200 | 3,290 | 3,160 | 2,730 |
| Vicat softening temperature | ISO 306:2022 | 85°C (185°F) | |||
| Water absorption rate | ISO 62:2008 | <0.1% | |||
| Stripping | N/A | No release agent required in standard uses | |||
| Cleaning | High-pressure water cleaning test (SGS witnessed) | Clean with soap and water by hand or high-pressure water jet. Tested at 1,000 bar for 15 minutes. | |||
Independently tested by SGS. Test report QDIN2603000391PL01_EN, 20 March 2026.
Leave the birch forests standing.
Extended reuse reduces board replacement frequency and associated material waste compared with short-life timber facing.
On-site repairability further extends service life.